Vol. 48 (2012), Issue 5, p. 49-57

Cu/Co-W Nanolayers Electrodeposited from Single Bath and their Mechanical Behaviour

Tsyntsaru N., Belevsky S., Cesiulis H., Dikusar A., Celis J.-P.

Abstract

УДК 620.3

For the first time thick (~ 8 µm) Cu/Co-W multilayered coatings with individual layers ranging from 5 to 200 nm were electrodeposited from a single bath. The content of tungsten in rich-in Co-W layers was controlled by varying current densities in a citrate-borate bath. Continuous Multi-Cycle (CMC) nanoindentation technique was used to analyze mechanical properties of those deposits. Optical examination of the indented zone revealed the absence of cracks inside and outside the indentation area in the interval of the normal loads used. The hardness of Cu/Co-W multilayers varied with the bi-layer period and the electrodeposition parameters. The Cu/Co-W multilayers showed an increased hardness compared to that of Co-W coatings electrodeposited under the same conditions.

Впервые были получены толстые (~ 8 мкм) Cu/Co-W многослойные покрытия из одной ванны с индивидуальными слоями от 5 до 200 нм. Содержание W в обогащенных Co-W слоях контролировалось изменением плотности тока при электроосаждении из цитрат-боратной ванны. Для анализа свойств таких покрытий использовано наноиндентирование непрерывным многоцикличным методом. Оптическая оценка зон индентирования показала отсутствие трещин как на внешней, так и внутренней областях индентирования в интервале использованных нагрузок на индентор. Показано, что твердость исследованных многослойных покрытий варьировала в зависимости от толщины индивидуальных слоев и параметров электроосаждения. Cu/Co-W покрытия обладали более высокой твердостью в сравнении с кобальт-вольфрамовыми, полученными в тех же условиях.

Download full-text PDF. 3523 downloads

Menu

Vol. 48 (2012), Issue 5, p. 49-57

Cu/Co-W Nanolayers Electrodeposited from Single Bath and their Mechanical Behaviour

Abstract