Surface Characterization of Anodically Treated β-Titanium Alloy for Biomedical Applications

Bhola R., Bhola S.M., Mishra B., Ayers R.A., Olson D.L., Ohno T.


Аннотация

УДК 544.65+617.3

 

The cellular response of anodically treated titanium alloys was investigated using cell attachment, morphological and surface analytical techniques. The behavior of a β Ti15Mo alloy has been compared with the conventional mixed alloy, Ti6Al4V and the α alloy, Ti2. Ti15Mo β alloy demonstrated a higher cell count and a thicker oxide on its surface. The presence of Ca and P was detected in all the alloys after the invitro cell culture test. TiO2 was present as the dominant oxide in all three alloys.

 

Исследована клеточная реакция на анодированные титановые сплавы анализированием клеточной адгезии, аналитическим изучением морфологии и характеристик поверхности сплавов. Характер изменений титанового деформируемого сплава β Ti 15 Mo сравнивали с изменениями традиционного соединения Ti 6 A l4 V и сплава α Ti 2. При использовании сплава β Ti 15 Mo выявлено более высокое количество клеток адгезии и более значительная толщина оксидной пленки на поверхности. Присутствие Ca и P было выявлено во всех сплавах после опытов in-vitro на культуре клеток. TiO2 оказался преобладающим оксидом во всех трех сплавах.

 

 
 

Скачать полнотекстовый PDF. 4269 скачиваний

Web-Design Web-Development SEO - eJoom Software. All rights reserved.