ELECTRICAL PRECISION TREATMENT OF MATERIALS

Electrodeposition of NiFe/Cu Multilayers from a Single Bath

Esmaili S., Bahrololoom M.E., Zamani C.


Abstract

УДК 541.138

 

NiFe/Cu multilayers were deposited from a single bath in the potentiostatic mode using two different solutions. In solution A, the ionic concentration ratios were Fe2+:Ni2+:Cu2+  9:60:10 and in solution B they were 1:103:1. To characterize the layers, scanning electron microscopy (SEM), high resolution transmission electron microscopy (HRTEM), X-ray diffraction (XRD) and atomic force microscopy (AFM) were used. SEM results revealed the layered structure of the deposits for relatively thick bilayers. While HRTEM provided direct evidence for the composition modulation across successive layers in the NiFe/Cu nanometer-multilayered structure prepared from solution B. Therefore, the layers prepared from solution B seemed to be more appropriate for giant magnetoresistance (GMR) applications. The effect of stirring during the electrodeposition process of the multilayers was also investigated.

 

Многослойные покрытия NiFe/Cu осаждались из одной ванны в потенциостатическом режиме с использованием двух различных растворов. В растворе А ионные соотношения концентраций были следующими: Fe2+:Ni2+:Cu2+ 9:60:10, а в растворе Б – 1:103:1. Для характеристики слоев применялись сканирующая электронная микроскопия (СЭМ), электронная микроскопия с высоким разрешением, рентгеноструктурный анализ и атомно-силовая микроскопия. Результаты, полученные с помощью СЭМ, показали наличие слоистой структуры покрытий в относительно толстых бислоях. Слои, приготовленные из раствора Б, оказались более подходящими для изготовления магнитосопротивлений. Влияние перемешивания во время процесса электроосаждения мультислоев было также исследовано.

 

 
 

Download full-text PDF. 4139 downloads

Web-Design Web-Development SEO - eJoom Software. All rights reserved.